Property

Test Method

Typical Value

Unit

Melt Flow Rate

ISO 1133 @ 190°C/2.16 kg

1.6

g/10 min

Melt Flow Rate

ISO 1133 @ 210°C/2.16 kg

3.7

g/10 min

Density

ISO 1183

1.19

g/cm3

Water vapor transmission rate

ASTM E96 @ 40°C 90RH

1.3

Oxygen transmission rate

@ 20°C 0RH

0.0059

Oxygen transmission rate

@ 20°C 65RH

0.0079

Oxygen transmission rate

@ 20°C 85RH

0.03

Tensile Strength at Break

ISO 527 @ 23°C

34

MPa

Tensile modulus

ISO 527 @ 23°C

2700

MPa

Elongation at Break

ISO 527 @ 23°C

15

%

Flexural modulus

ISO 178 @ 23°C

4800

MPa

Simply Supported Beam Unnotched Impact

ISO 179

2

Kj/m2

Hardness

ISO 2023

90

Crystallization temperature

ISO 11357

158

Glass transition temperature

ISO 11357

57

℃

Melting temperature

ISO 11357

183

℃